选择丙烯酸乳液作为成膜物质,磷酸锌和氧化铁红作为防锈颜料,研究了乳液种类及用量、磷酸锌用量对水性丙烯酸防腐涂料性能的影响。加入丁醚作为快干剂,研究其用量对水性丙烯酸防腐涂料干燥速度的影响。结果表明:当苯丙乳液用量为40%、磷酸锌与氧化铁红比例为1∶1且用量为5%、丁醚用量为0.3%时,所制得的水性丙烯酸快干防腐涂料综合性能最优。

Acrylic emulsion was selected as film-forming material, zinc phosphate and iron oxide red were used as antirust pigments, and the effects of the type and amount of lotion and the amount of zinc phosphate on the performance of waterborne acrylic anti-corrosive coatings were studied. Add butyl ether as a quick drying agent and study the effect of its dosage on the drying rate of waterborne acrylic anti-corrosion coatings. The results showed that when the content of styrene acrylic lotion was 40%, the ratio of zinc phosphate to ferric oxide red was 1∶1 and 5%, and the content of butyl ether was 0.3%, the comprehensive performance of the waterborne acrylic fast drying anti-corrosion coating was the best.