Acrylic emulsion was selected as film-forming material, zinc phosphate and iron oxide red were used as antirust pigments, and the effects of the type and amount of lotion and the amount of zinc phosphate on the performance of waterborne acrylic anti-corrosive coatings were studied. Add butyl ether as a quick drying agent and study the effect of its dosage on the drying rate of waterborne acrylic anti-corrosion coatings. The results showed that when the content of styrene acrylic lotion was 40%, the ratio of zinc phosphate to ferric oxide red was 1∶1 and 5%, and the content of butyl ether was 0.3%, the comprehensive performance of the waterborne acrylic fast drying anti-corrosion coating was the best.