关于客车结构受力类腻子开裂问题的原因分析及对策

杨海涛[1]

PDF(3268 KB)

现代涂料与涂装 ›› 2022, Vol. 25 ›› Issue (8) : 41-43.

关于客车结构受力类腻子开裂问题的原因分析及对策

杨海涛[1]

作者信息 +

The Reasons for Bus Structure Type of Putty Crack Problem Analysis and Countermeasures

YANG Hai-tao[1]

Author information +

文章历史 +

摘要

针对容车存在的3个典型结构受力类腻子轩裂问题案例,结合问题现状及原因分析,制定相关解决措施,较好地解决了腻子开裂问题,进一步提高本辆漆面细节处理质量。

Abstract

Aiming at three typical structure of bus and coach class puty crack problem cases,combined with the situation and causes of the problem analysis,the relevant solutions were formulated,the problem of the putty crack was well solved,the quality of the vehicle paint detail processing was improved.

导出引用

杨海涛[1]. 关于客车结构受力类腻子开裂问题的原因分析及对策[J]. 现代涂料与涂装. 2022, 25(8): 41-43

YANG Hai-tao[1]. The Reasons for Bus Structure Type of Putty Crack Problem Analysis and Countermeasures[J]. Modern Paint & Finishing. 2022, 25(8): 41-43

中图分类号： TQ639