客车校车后视镜座处漆面开裂成因及优化措施

杨海涛[1]

作者信息 +

Causes and Optimization Measures of Paint Surface Cracking on School Bus Rear ViewMirror Seats

YANG Hai-tao[1]

Author information +

文章历史 +

摘要

针对客车校车后视镜座处的典型漆面开裂问题,排查分析了其产生原因。通过制定改善方案,典型漆面开裂问题得到较好改善,并成功申报了一项实用新型发明专利。

Abstract

Aiming at the typical paint surface cracking problem at the bus rearview mirror seat,the causes was analyzed.Through the formulation of the improvement plan,the typical paint surface cracking problem was improved,and a utility model invention patent was successfully applied.